Studying structural properties of polyethylene waxes with infrared spectroscopy
Subject Areas :
Mina
Alizadehaghdam
1
(دانشگاه صنعتی سهند تبریز، پژوهشکده مواد پلیمری و دانشکده مهندسی پلیمر)
Keywords: polyethylene wax, branching degree, oxidation, unsaturation, crystallinity,
Abstract :
Polyethylene waxes are ethylene oligomers with unique properties, high crystallinity, linearity and low solubility in the solvents which provides a variety of applications in different industries such as electrotechnique, rubber, textile, fertilizer production, etc. Infrared spectroscopy (FTIR) is a simple and common analysis to examine the chemical and physical properties of polyethylene such as structure identification, chemical composition and crystallinity evaluation. Physical properties of a polyethylene wax largely depends on its branching degree. Absorption at the wavelength 1378 cm-1 associated with methyl groups symmetric deformation is used for determining the number of branches. Rocking vibration of methyl and methylene groups in the wavelength ranges of 800-1200 cm-1 and 720-770 cm-1 respectively are applied for identification of the branch type. Absorption of vinyl, trans vinylene and vinylidene unsaturation and carbonyl groups introduced into the structure by wax oxidation, were investigated. Absorption intensity was related to the number of absorbing species by molar absorption parameter or absorption coefficient based on the Beer-Lambert law. Some experimental relations were also introduced based on nuclear magnetic resonance spectroscopy. Deconvolution of the double absorption in the range 720-730 cm-1, associated with rocking vibration of methylene groups, to the crystalline and amorphous bands led to the crystallinity estimation.
1. Ciesińska W., Liszyńska B., Zieliński J., Selected Thermal Properties of Polyethylene Waxes, Journal of Thermal Analysis and Calorimetry, 125(3), 1439-1443, 2016.
2. YETGİN S., Characterization of Lubricant Polyethylene Waxes, European Journal of Technique (EJT), 10(2), 489-500, 2020.
3. Gulmine J.V., Janissek P.R., Heise H.M., Akcelrud L., Polyethylene Characterization by FTIR, Polymer Testing, 21(5), 557-563, 2002.
4. Prasad A., A Quantitative Analysis of Low Density Polyethylene and Linear Low Density Polyethylene Blends by Differential Scanning Calorimetery and Fourier Transform Infrared Spectroscopy Methods, Polymer Engineering & Science, 38(10), 1716-1728, 1998.
5. Wang X., Han X., Ren F., Xu R., Bai Y., Porous Organic Polymers-Supported Metallocene Catalysts for Ethylene/1-Hexene Copolymerization, Catalysts, 8(4), 146, 2018.
6. Blitz J.P., McFaddin D.C., The Characterization of Short Chain Branching in Polyethylene Using Fourier Transform Infrared Spectroscopy, Journal of Applied Polymer Science, 51(1),13-20, 1994.
7. Cran M.J., Bigger S.W., Quantitative Analysis of Polyethylene Blends by Fourier Transform Infrared Spectroscopy, Applied Spectroscopy, 57(8), 928-932, 2003.
8. de Kock R.J., Hol P.A.H.M., Bos H., Infrared Determination of Unsaturated Bonds in Polyethylene, Fresenius' Zeitschrift für analytische Chemie, 205(1), 371-381, 1964.
9. Gardette M., Perthue A., Gardette J.-L., Janecska T., Földes E., Pukánszky B., Therias S., Photo- and Thermal-Oxidation of Polyethylene: Comparison of Mechanisms and Influence of Unsaturation Content, Polymer Degradation and Stability, 98(11), 2383-2390, 2013.
10. Materials A.S.f.T., Standard Practice for Determination of Structural Features in Polyolefins and Polyolefin Copolymers by Infrared Spectrophotometry Designation D5576-00. 2000.
11. Materials A.S.f.T., Standard Test Method for Vinylidene Unsaturation in Polyethylene by Infrared Spectrophotometry Designation D3124-98. 2019.
12. Usami T., Takayama S., Identification of Branches in Low-Density Polyethylenes by Fourier Transform Infrared Spectroscopy, Polymer Journal, 16(10), 731-738, 1984.
13. Materials A.S.f.T., Standard Test Methods for Absorbance of Polyethylene Due to Methyl Groups1 at 1378 cm-1 Designation D2238-22. 2022.
14. Popov V.P., Branching of Low-Pressure Polyethylene, Journal of Applied Spectroscopy, 15(6), 1669-1670, 1971.
15. Teranishi K., Sugahara K., The Studies of the Branching and the Crystallinity in Polyethylene by Infrared-method, Kobunshi Kagaku, 23(255), 512-520, 1966.
16. Panin A.N., Sukhova T.A., Bravaya N.M., Triisobutylaluminum as Cocatalyst for Zirconocenes. I. Sterically Opened Zirconocene/Triisobutylaluminum/Perfluorophenylborate as Highly Effective Ternary Catalytic System for Synthesis of Low Molecular Weight Polyethylenes, Journal of Polymer Science Part A: Polymer Chemistry, 39(11), 1901-1914, 2001.
17. Umare P.S., Rao K., Tembe G.L., Dhoble D.A., Trivedi B., Polyethylene Waxes: Catalytic Synthesis by Ti‐Biphenolates, Journal of Macromolecular Science, Part A, 44(9), 977-987, 2007.
18. Arnaud R., Moisan J.Y., Lemaire J., Primary Hydroperoxidation in Low-Density Polyethylene, Macromolecules, 17(3), 332-336, 1984.
19. Blom R., Follestad A., Noel O., Kinetics of Chain Transfer During Eethylene Polymerization with Chromium Oxide/Silica Catalyst, Journal of Molecular Catalysis, 91(2), 237-249, 1994.
20. Jianyu Z., Yongjie Y., Jinsheng G., Jianhang X., Developement of Oxidized Polyethylene Waxes, Petroleum Science and Technology, 18(9-10), 1077-1088, 2000.
21. MallapragadaS.K., Narasimhan B., Infrared Spectroscopy in the Analysis of Polymer Crystallinity, in Encyclopedia of Analytical Chemistry. 2022. p. 1-16.
22. Hagemann H., Snyder R., Peacock A., Mandelkern L., Quantitative Infrared Methods for the Measurement of Crystallinity and its Temperature Dependence: Polyethylene, Macromolecules, 22(9), 3600-3606, 1989.